SikaBond®-234 Maxtack
SikaBond®-234 Maxtack is a one-component, water-based construction adhesive with good initial grab that forms a strong permanent bond to most construction materials.
- High initial tack
- Fixing without tapes, nails or screws
- Good adhesion on many substrates
- Good workability
- Easy to tool and clean up
- Water-based
- Over-paintable by an emulsion waterborne paint
Usage
- Indoor and sheltered outdoor use.
- Wall and ceiling
- Porous substrates such as wood, concrete, brick, mortar, stone, tile, fiber-cement, plasterboard etc.
- Non-porous substrates such as steel, aluminum, other metals, Rigid PVC, and polystyrene
*At least one of the substrates should be porous to allow drying of the adhesive
Advantages
- High initial tack
- Fixing without tapes, nails or screws
- Good adhesion on many substrates
- Good workability
- Easy to tool and clean up
- Water-based
- Over-paintable by an emulsion waterborne paint
Packaging
300 ml / cartridge (12 cartridges per box)
75 g / piece (12 pieces per box)
Colour
Off-white
Product Details
Composition
1-Component water-based dispersion
Shelf life
Minimum 18 months from the production date, if storage conditions are met and the packaging is in its original sealed and undamaged state.
Storage conditions
SikaBond®-234 Maxtack shall be stored in dry conditions, protected from direct sunlight and at temperatures between +5 °C and +25 °C.
Density
1.34 g/ml approx..
Shore A hardness
75 approx.(after 28 days) | ISO 868 |
Lap shear strength
2.8 N/mm2
Service temperature
−30 °C to +60 °C
Application
Sagging
Very low | (ISO 7930) |
Substrate temperature
+5 °C to +35 °C
Open Time
5 Min (23 °C / 50% r.h.) |
Curing rate
24 – 72 hrs for final cure (23 °C / 50% r.h.) | (CQP 049-2) |
Consumption
Using a nozzle with a 5 mm diameter, bead yield is approx 14 m in length per 300 ml cartridge (approx. 20 ml per linear meter).
APPLICATION INSTRUCTIONS
For the application of SikaBond®-234 Maxtack all standard construction guidelines apply.
SUBSTRATE PREPARATION
The substrate must be clean, dry, sound and homogeneous, free from oils, grease, dust and loose or friable particles. Paint, cement laitance and other poorly adhering contaminants must be removed. SikaBond®-234 Maxtack adheres without primers and/or activators.
Non-porous substrates
Aluminium, anodised aluminium, stainless steel, PVC, galvanised steel, powder coated metals or glazed tiles have to be cleaned and pre-treated using Sika® Aktivator-205, wiped on with a clean towel. Before sealing, allow a flash-off time of > 15 minutes (< 6 hours).
Other metals, such as copper, brass and titanium-zinc, also have to be cleaned and pre-treated using Sika® Aktivator-205,wiped on with a clean towel. After the necessary flash-off time, use a brush to apply Sika® Primer-3 N and allow a further flash-off time of > 30 minutes (< 8 hours) before sealing the joints.
Porous substrates
Wood has to be sanded, concrete and mortar have to be scrubbed and sanded to remove laitance.
Clean with an industrial vacuum.
For more detailed advice and instructions please contact our Technical Service Department.
CLEANING OF EQUIPMENT
Clean all tools and application equipment immediately after use with water. Once cured, residual material can only be removed mechanically.
VDO